1. A MIXTURE OF REFRACTORY CLAYS OF CB 3-3. CHEMICAL COMPOSITION: AL2O3-25 07%; FE2O3-1 50%; TIO2-1 27%; HUMIDITY - 1 8%; NETWORK SITTING 0.063 -1 90%; PP PP - 7 03%; T TOTAL (FIRE RESISTANCE) - 1 580 GRAD. WITH; TU 1 4. 2-24655289-004: 201 0. A DEPOSIT IS VISIBLE. PURPOSE: FOR USE IN PRODUCTION CONDITIONS IN THE TECHNOLOGY OF MANUFACTURING OF REFRACTORY REFINING CERAMIC MATERIALS AND PRODUCTS.
1. A MIXTURE OF REFRACTORY CLAYS OF CB 3-3. CHEMICAL COMPOSITION: AL2O3-25 07%; FE2O3-1 50%; TIO2-1 27%; HUMIDITY - 1 8%; NETWORK SITTING 0.063 -1 90%; PP PP - 7 03%; T TOTAL (FIRE RESISTANCE) - 1 580 GRAD. WITH; TU 1 4. 2-24655289-004: 201 0. A DEPOSIT IS VISIBLE. PURPOSE: FOR USE IN PRODUCTION CONDITIONS IN THE TECHNOLOGY OF MANUFACTURING OF REFRACTORY REFINING CERAMIC MATERIALS AND PRODUCTS.
08-July-2019
2508300000
1. MIXTURE OF FIRE-RESISTANT CLAYS OF ST. BRAND 2-2. CHEMICAL COMPOSITION: AL2O3-23.37%; FE2O3-0.86%; TIO2-1 31%; HUMIDITY - 1 7%; BALANCE ON SITES WITH GRID 0.063 -3.39%; PPP - 6.43%; T TOTAL (FIRE RESISTANCE) - 1 580 GRADES. WITH; TU 1 4. 2-24655289-004: 201 0. DEPOSIT
1. MIXTURE OF FIRE-RESISTANT CLAYS OF ST. BRAND 2-2. CHEMICAL COMPOSITION: AL2O3-23.37%; FE2O3-0.86%; TIO2-1 31%; HUMIDITY - 1 7%; BALANCE ON SITES WITH GRID 0.063 -3.39%; PPP - 6.43%; T TOTAL (FIRE RESISTANCE) - 1 580 GRADES. WITH; TU 1 4. 2-24655289-004: 201 0. DEPOSIT
11-July-2019
2508300000
1. MIXTURE OF FIRE-RESISTANT CLAYS OF ST. BRAND 2-2. CHEMICAL COMPOSITION: AL2O3-23.81%; FE2O3-0.95%; TIO2-1 63%; HUMIDITY - 1 6%; BALANCE ON SITES WITH GRID 0.063 -3.48%; PPP - 6.52%; T TOTAL (FIRE RESISTANCE) - 1 580 GRADES. WITH; TU 1 4. 2-24655289-004: 201 0. DEPOSIT
1. MIXTURE OF FIRE-RESISTANT CLAYS OF ST. BRAND 2-2. CHEMICAL COMPOSITION: AL2O3-23.81%; FE2O3-0.95%; TIO2-1 63%; HUMIDITY - 1 6%; BALANCE ON SITES WITH GRID 0.063 -3.48%; PPP - 6.52%; T TOTAL (FIRE RESISTANCE) - 1 580 GRADES. WITH; TU 1 4. 2-24655289-004: 201 0. DEPOSIT
21-July-2019
2508300000
1. MIXTURE OF FIRE-RESISTANT CLAYS OF ST. BRAND 2-2. CHEMICAL COMPOSITION: AL2O3-23.00%; FE2O3-0.88%; TIO2-1 59%; HUMIDITY - 1 6%; BALANCE ON SITES WITH GRID 0.063 -4.00%; PPP - 6.26%; T TOTAL (FIRE RESISTANCE) - 1 580 GRADES. WITH; TU 1 4. 2-24655289-004: 201 0. DEPOSIT
1. MIXTURE OF FIRE-RESISTANT CLAYS OF ST. BRAND 2-2. CHEMICAL COMPOSITION: AL2O3-23.00%; FE2O3-0.88%; TIO2-1 59%; HUMIDITY - 1 6%; BALANCE ON SITES WITH GRID 0.063 -4.00%; PPP - 6.26%; T TOTAL (FIRE RESISTANCE) - 1 580 GRADES. WITH; TU 1 4. 2-24655289-004: 201 0. DEPOSIT